Sharadaa Ceramics Sharada RFC-90 Gel Bonded Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | Sharada |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics Sharada RFC-90 Gel Bonded Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mullite Bonded Free Flowing Cement Free Versatile Castable SystemProduct Characteristics: High Mullitisation, Free from Low Temperature eutectics, Non wetting to molten metals Ferrous/Non Ferrous, Extreme resistance to thermal, Ultra high creep resistance-High HMOR, Intricate shaped Precast blocks superior to fired and Resistance to Mill scale /AccretionIndustry Focus: Steel: Blast Furnace Trough, Torpedo Ladles, Lances/Snorkel, Burner Blocks, Reheat furnace roof/Hearth, Coke Oven door/Roof Repair, Sponge Iron DRI Maintenance, Tundish Flow control device/Well blocks/Nozzles; Cement: Burner Pipe; Non Ferrous: Non wetting to Aluminum/Copper, Lined in Melting furnace walls, Launders, Aluminum Transfer Ladles; Ceramic: Fused silica kiln furniture for Ultra Low thermal, Expansion and High resistance to thermal shock; Ferrous Foundry: Ladles; Glass: Repair of Silica Roof, Sub paving.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.70 g/cc @Temperature 1400 °C |
0.0975 lb/in³ @Temperature 2550 °F |
|
| 2.80 g/cc @Temperature 800 °C |
0.101 lb/in³ @Temperature 1470 °F |
||
| 2.90 g/cc @Temperature 200 °C |
0.105 lb/in³ @Temperature 392 °F |
||
| Porosity | 13 % | 13 % | |
| 14 % | 14 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.180 GPa @Temperature 1400 °C |
26.1 ksi @Temperature 2550 °F |
Hot |
| Compressive Strength | 58.8 MPa @Temperature 800 °C |
8530 psi @Temperature 1470 °F |
Cold Crushing |
| 78.5 MPa @Temperature 1400 °C |
11400 psi @Temperature 2550 °F |
Cold Crushing |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 90 % | 90 % | |
| Fe2O3 | 1.0 % | 1.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Base Material | Brown Fused Alumina | |
| Permanent Linear Change | -1.0 - 1.0% | 1400°C |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2115 Amorphous Polyalphaolefin (APAO)
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours
- Sichuan Deyang Haton® hCF31 Polyphenylene Sulfide
- Techmer ES HiFill® PA12 GF50 L 50% Glass Filled
- Lubrizol Estane® AG 9550 Thermoplastic Polyurethane
- Fainplast Compounds HGA 40 Flexible PVC, Sheathing for High Temperatures
- 3M 21825 Industrial Polyethylene Temporary Surface Protection Tape
- Arkema Group ORGASOL® 2002 EXD Nat 1 Polyamide 12, Food Contact Approved
- C.O.I.M. EXTER S® S 402 Isophthalic Resin
Copyright © lookpolymers.com All Rights Reserved