BASF Ultramid® HPN 9350 HS PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® HPN 9350 HS PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid HPN 9350 HS is a flexible, heat stabilized, impact modified PA6 extrusion grade resin. It possesses a balance of performance properties such as good flexibility, toughness and abrasion resistance. The addition of heat stabilizer system extends its retention of properties at elevated temperatures. Chemical resistance is excellent to greases, oils, and hydrocarbons.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Water Absorption 6.8 %
6.8 %
ISO 62
Moisture Absorption at Equilibrium 1.9 %
1.9 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80
80
ASTM Test
Tensile Strength, Yield 45.0 MPa
6530 psi
50mm/min; ISO 527
50.0 MPa
7250 psi
2 in/min; ASTM Test
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
2 in/min; ASTM Test
Elongation at Yield 4.5 %
4.5 %
50mm/min; ISO 527
5.0 %
5.0 %
2 in/min; ASTM Test
Tensile Modulus 1.70 GPa
247 ksi
1mm/min; ISO 527
Flexural Strength 50.0 MPa
7250 psi
ISO Data
69.0 MPa
10000 psi
ASTM Test
9.50 MPa

@Temperature 120 °C
1380 psi

@Temperature 248 °F
ASTM Test
10.0 MPa

@Temperature 93.0 °C
1450 psi

@Temperature 199 °F
ASTM Test
15.0 MPa

@Temperature 65.0 °C
2180 psi

@Temperature 149 °F
ASTM Test
105 MPa

@Temperature -40.0 °C
15200 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 1.45 GPa
210 ksi
ISO Data
1.73 GPa
251 ksi
ASTM Test
0.190 GPa

@Temperature 120 °C
27.6 ksi

@Temperature 248 °F
ASTM Test
0.220 GPa

@Temperature 93.0 °C
31.9 ksi

@Temperature 199 °F
ASTM Test
0.375 GPa

@Temperature 65.0 °C
54.4 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 5.90 J/cm

@Thickness 3.17 mm
11.1 ft-lb/in

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
55.0 °C
131 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Extrusion
Processing Profile Extrusion
Sheet extrusion
Special characteristic Heat stabilized or stable to heat