A. Schulman ComAlloy Lubrilon® 640 Nylon 6/12, PTFE Reinforced, Flow Enhanced

Category	Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612 with PTFE Filler
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 640 Nylon 6/12, PTFE Reinforced, Flow Enhanced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³
Linear Mold Shrinkage	0.016 cm/cm	0.016 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	109	109	ASTM D785
Tensile Strength, Ultimate	52.0 MPa	7540 psi	ASTM D638
Elongation at Break	30 %	30 %	ASTM D638
Flexural Strength	74.0 MPa	10700 psi	ASTM D790
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm	0.899 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.39 J/cm	10.1 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	195 - 215 °C	383 - 419 °F
Deflection Temperature at 0.46 MPa (66 psi)	174 °C	345 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	74.0 °C	165 °F	ASTM D648