BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 - 2.2 % | 1.8 - 2.2 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number; ISO 307 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 33.3 g/10 min @Load 5.00 kg, Temperature 275 °C |
33.3 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 5.30 GPa | 769 ksi | ISO 527 |
| Flexural Strength | 89.6 MPa | 13000 psi | ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 3000 MPa | 435000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 180 °C | 356 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.8 @Frequency 1.00e+6 Hz |
6.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz |
0.20 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75N Fluoroelastomer Compound
- Quadrant EPP Ertalon® 6XAU+ PA 6, heat stabilized, cast (ISO Data)
- Advanced Elastomer Systems Santoprene® 8281-65 Thermoplastic Rubber (discontinued **)
- Polimeri Europa EDISTIR N1461 Polystyrene (discontinued **)
- IBC Advanced Alloys 4% BeCu Beryllium Copper Master Alloy
- Chase Plastics CP Pryme® NN143GL (DAM) Nylon 66, 43% Glass Fiber Reinforced, Internally Lubricated
- Dow Buna® SB 1721 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- Dow DMDB-7950 NT 7 High Density Polyethylene Resin
- DuPont Teijin Films Melinex® 339 Polyester Film, 1000 Gauge
- 3M Scotch® 3771 Standard Message Box Sealing Tape
Copyright © lookpolymers.com All Rights Reserved