Chi Mei Wonderloy® PC-345 PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Wonderloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Wonderloy® PC-345 PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 1.20 kg, Temperature 300 °C |
13 g/10 min @Load 2.65 lb, Temperature 572 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 80 % | 80 % | 50 mm/min; ISO 527 |
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | ISO 180/4A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | annealed; ISO 75 |
| 106 °C | 223 °F | unannealed; ISO 75 | |
| Vicat Softening Point | 110 °C @Load 5.00 kg |
230 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 125 °C @Load 1.00 kg |
257 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0590 in |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-752 Epoxy Prepreg, 6K 5HS 630-500 Reinforced
- Dielectric Polymers NT-5521-2 Photo Processing Tape (discontinued **)
- PolyOne Edgetek® LCP-30GF/000 Liquid Crystal Polymer - 30% Glass Fiber (discontinued **)
- Lehmann & Voss LUVOCOM® 1100-8401 Polyether sulfone, unreinforced
- SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer
- Loctite® 5083 Silicone Light Cure Adhesive
- CP-Polymer-Technik Wellamid® 6000/42 GV 15 HWCP 15% Glass Fiber Nylon 6, Polymer Modified, Heat Stabilized, Conditioned
- Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
- Ceradyne Ceralloy® 147-5 Silicon Nitride
Copyright © lookpolymers.com All Rights Reserved