BASF Ultramid® B3ZG3 BK 30564 15% Glass Filled PA6-1 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3ZG3 BK 30564 15% Glass Filled PA6-1 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Impact-modified and 15% glass fiber reinforced injection-molding grade, for instance, for automotive cable conduits.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 7.2 - 7.8 % | 7.2 - 7.8 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 2.1 - 2.7 % | 2.1 - 2.7 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 160 | 160 | ISO 307 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | restricted |
| Melt Flow | 42.7 g/10 min @Load 5.00 kg, Temperature 275 °C |
42.7 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 18 % | 18 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 2.90 GPa | 421 ksi | ISO 527-1/-2 |
| Flexural Strength | 80.0 MPa | 11600 psi | at max force; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 180 °C | 356 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00 Hz |
6.2 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz |
0.20 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 30564 | |
| Commercial Status | Europe |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP300C Sheet and Thermoforming Grade Polypropylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBTS
- Techmer ES HiFill® HDPE GF30 A1 30% Glass Filled
- Silberline Aquavet® 205-136M
- Polyram PlusTek RA102 Nylon 6.6, General Purpose
- Eagle Brass 220 Commercial Bronze, 3/4 Hard
- Diamond Polymers Softflex® 8200
- Hippe EP CC 31 Woven Cotton Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod
- Eurotec® Tecomid® NB30 MF30 BK001 HS PA6, 30% mineral reinforced, heat stabilized, black
Copyright © lookpolymers.com All Rights Reserved