BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 6.3 - 6.9 %
6.3 - 6.9 %
ISO 62
Moisture Absorption at Equilibrium 1.9 - 2.3 %
1.9 - 2.3 %
ISO 62
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
Melt Flow 68 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 68 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 185 MPa
26800 psi
ISO 527-1/-2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527-1/-2
Flexural Strength 270 MPa
39200 psi
ISO 178
Flexural Modulus 8.60 GPa
1250 ksi
ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
15.5 kJ/m²

@Temperature 23.0 °C
 7.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 - 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 11.1 - 13.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 33.3 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
DIN 52612-1
Melting Point 220 °C
428 °F
ISO 11357-1/-3
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
165 °C
329 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.023

@Frequency 1.00e+6 Hz
 0.023

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 575 V
575 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection Molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929