BASF Novolen® 1148 UC Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer BASF
Trade Name Novolen®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Novolen® 1148 UC Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nucleated grade with antistatic agent for injection molded parts.Data was collected by ISO methods and provided by BASF.
Physical Properties Metric English Comments
Density 0.910 g/cc
0.0329 lb/in³
Water Absorption 0.10 %
0.10 %
Moisture Absorption at Equilibrium 0.10 %
0.10 %
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
Melt Flow 101 g/10 min

@Load 2.16 kg,
Temperature 230 °C
101 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
Elongation at Break 20 %
20 %
Elongation at Yield 9.0 %
9.0 %
Tensile Modulus 1.70 GPa
247 ksi
Charpy Impact Unnotched 7.80 J/cm²
37.1 ft-lb/in²
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
0.150 J/cm²

@Temperature -30.0 °C
0.714 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 135 µm/m-°C

@Temperature 20.0 °C
75.0 µin/in-°F

@Temperature 68.0 °F
Melting Point 163 °C
325 °F
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 95.0 °C
203 °F
Flammability, UL94 HB

@Thickness 0.790 mm
HB

@Thickness 0.0311 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
Dielectric Constant 2.3

@Frequency 100 Hz
2.3

@Frequency 100 Hz
2.3

@Frequency 1e+6 Hz
2.3

@Frequency 1e+6 Hz
Dielectric Strength 140 kV/mm
3560 kV/in
Dissipation Factor 0.00081

@Frequency 100 Hz
0.00081

@Frequency 100 Hz
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
Comparative Tracking Index 600 V
600 V