BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 4.7 - 5.3 % | 4.7 - 5.3 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.4 - 1.8 % | 1.4 - 1.8 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 145 cm³/g | 145 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ISO 307 |
| Melt Flow | 49.3 g/10 min @Load 5.00 kg, Temperature 275 °C |
49.3 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 150 MPa | 21800 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | ISO178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 10.5 J/cm² | 50.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 6650 MPa | 965000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 260 °C | 500 °F | DIN 53765 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20,000 hr |
| 165 °C | 329 °F | for 50% loss of tensile strength after 5,000 hr | |
| 240 °C | 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 5.7 @Frequency 1.00e+6 Hz |
5.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.15 @Frequency 1.00e+6 Hz |
0.15 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| NSF Std. 61 | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJLF112L Polyvinyl Chloride, Flexible (PVC, Flexible)
- FiberNide Nickel Aluminide Foam Atomic 20% Aluminum
- LG Chemical AF342T ABS, Flame Retardant, High Impact
- KaMin KaMin® 90 Kaolin clay - Waterwashed
- SSAB Tunnplat Domex® 024 BOR Water quenched Boron Steel
- SABIC Innovative Plastics Valox® 830 PBT (Europe-Africa-Middle East)
- Dow Corning 9-1363 INDUSTRIAL ASSEMBLY ADHESIVE SEALANT
- Entec Hypro™ PP-CP4/2 Impact Copolymer, 4 Melt Flow
Copyright © lookpolymers.com All Rights Reserved