BASF Ultramid® 8350 HS PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8350 HS PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility. It is also available in non-heat stabilized (Ultramid 8350) and/or pigmented versions.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
6.7 %
6.7 %
ISO 62
Moisture Absorption at Equilibrium 1.9 %
1.9 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 78
78
ASTM Test
Tensile Strength, Yield 53.0 MPa
7690 psi
50mm/min; ISO 527
53.0 MPa
7690 psi
2 in/min; ASTM Test
14.0 MPa

@Temperature 120 °C
2030 psi

@Temperature 248 °F
ISO Data
14.0 MPa

@Temperature 120 °C
2030 psi

@Temperature 248 °F
ASTM Test
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ASTM Test
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ISO Data
85.0 MPa

@Temperature -40.0 °C
12300 psi

@Temperature -40.0 °F
ASTM Test
85.0 MPa

@Temperature -40.0 °C
12300 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
2 in/min; ASTM Test
Elongation at Yield 5.0 %
5.0 %
50mm/min; ISO 527
5.0 %
5.0 %
2 in/min; ASTM Test
8.0 %

@Temperature -40.0 °C
8.0 %

@Temperature -40.0 °F
ASTM Test
8.0 %

@Temperature -40.0 °C
8.0 %

@Temperature -40.0 °F
ISO Data
27 %

@Temperature 120 °C
27 %

@Temperature 248 °F
ISO Data
27 %

@Temperature 120 °C
27 %

@Temperature 248 °F
ASTM Test
37 %

@Temperature 80.0 °C
37 %

@Temperature 176 °F
ISO Data
37 %

@Temperature 80.0 °C
37 %

@Temperature 176 °F
ASTM Test
Tensile Modulus 1.80 GPa
261 ksi
1mm/min; ISO 527
0.150 GPa

@Temperature 120 °C
21.8 ksi

@Temperature 248 °F
ISO Data
0.210 GPa

@Temperature 80.0 °C
30.5 ksi

@Temperature 176 °F
ISO Data
2.15 GPa

@Temperature -40.0 °C
312 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 50.0 MPa
7250 psi
ISO Data
65.0 MPa
9430 psi
ASTM Test
10.0 MPa

@Temperature 120 °C
1450 psi

@Temperature 248 °F
ASTM Test
10.0 MPa

@Temperature 93.0 °C
1450 psi

@Temperature 199 °F
ASTM Test
20.0 MPa

@Temperature 65.0 °C
2900 psi

@Temperature 149 °F
ASTM Test
120 MPa

@Temperature -40.0 °C
17400 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 1.75 GPa
254 ksi
ISO Data
1.80 GPa
261 ksi
ASTM Test
0.165 GPa

@Temperature 120 °C
23.9 ksi

@Temperature 248 °F
ASTM Test
0.210 GPa

@Temperature 93.0 °C
30.5 ksi

@Temperature 199 °F
ASTM Test
0.270 GPa

@Temperature 65.0 °C
39.2 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 1.90 J/cm

@Temperature -40.0 °C
3.56 ft-lb/in

@Temperature -40.0 °F
ASTM Test
NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 10.0 J/cm²
47.6 ft-lb/in²
ISO 179
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 106 µm/m-°C

@Temperature -30.0 - 30.0 °C
58.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
ASTM Test
145 °C
293 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 51.0 °C
124 °F
ISO 75
56.0 °C
133 °F
ASTM Test
Flammability, UL94 HB
HB
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding
Mold Temperature 70.0 °C
158 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Extrusion
Processing Injection Molding
Other Extrusion
Profile extrusion
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes