Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
Mytex Polymers AN18KW-01 FK Polypropylene, Rubber modified Description: Rubber modified polypropylene produced for automotive interior applications using Mytex® Technology. Specifically designed to achieve ductile performance at cold temperatures during a.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering Q70X Polyurethane Rubber Peroxide cured, self-lubricating, Polyurethane Rubber, 65-75 °IRHD. Compounded with graphite or molyb-d. To meet ASTM line call-out M5BG714, B14, EO14, EO34. Polyester-based urethane. ASTM & ISO d.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering Q70Y Polyurethane Rubber Peroxide cured, yellow Polyurethane Rubber, 65-75 °IRHD. Polyester-based urethane. To meet ASTM line call-out M5BG714, B14, EO14, EO34. ASTM & ISO designation = AU.Applications: Excellent abrasio.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering R60D Natural Rubber Natural Rubber, 55-65 °IRHD. Formulated to Defence Standard 93-30, Type QX, Grade 60 (NRQX60).Applications: Natural rubber offers low compression set, high tensile strength, high resilience and ex.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V80B Fluoroelastomer Compound Fluoroelastomer Rubber, 76-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK814, A1-10, B37, B38, EF31, EO78, F15, Z1. Where Z1 = compressi.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V80H Fluoroelastomer Compound Fluoroelastomer Rubber, 75-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Adminis.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D412 |
Precision Polymer Engineering V90G Fluoroelastomer Compound Green Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M3HK914, A1-10, B38, EF31, EO78, Z1, Z2. Z1 = colour green, .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
NOVA Chemicals Sclair® 2318 LLDPE Injection Molding Resin
(discontinued **) Features: Low odor, low warpage, fast cycling, high surface gloss, permits light weight lid design.Applications: Thin walled container lids and closures.Data provided by the manufacturer. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE7076 Profile Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields parts with high gloss and excellent stiffness.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 u.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Petroquimica Triunfo Trithene® CX 8087 MDPE - Cast Film The Trithene CX 8087 resin is a medium density polyethylene (MDPE) with medium molecular weight that presents excellent balance between mechanical properties, processability and stiffness, allowing .. |
|||
Tensile Strength, Yield | 14.0 - 32.0 MPa | 2030 - 4640 psi | Average value: 25.1 MPa Grade Count:55 |
Overview of materials for Polypropylene with 20% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini.. |
|||
Tensile Strength, Yield | 14.0 - 35.0 MPa | 2030 - 5080 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31008 PVDF Copolymer
(discontinued **) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Yield | 14.0 - 35.0 MPa | 2030 - 5080 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 32008 PVDF Copolymer
(Unverified Data**) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Yield | 14.0 - 20.0 MPa | 2030 - 2900 psi | Average value: 16.6 MPa Grade Count:5 |
Overview of materials for Polytetrafluoroethylene (PTFE), Bronze Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Bronze Filled". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Yield | 14.0 MPa @Strain 0.200 %, Temperature 1150 °C |
2030 psi @Strain 0.200 %, Temperature 2100 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ ETA-3104HF Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, good impact and stiffness balance, good dimensional stability, good processabilityApplications: molded-in color.. |
|||
Tensile Strength, Yield | 14.0 - 35.0 MPa @Thickness 2.00 mm |
2030 - 5080 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional .. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP) LNP* THERMOCOMP* 2X00858 is a compound based on FEP resin containing proprietary fillers. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP) LNP* THERMOCOMP* 2X03624H is a compound based on FEP resin containing Proprietary Filler(s). |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SSH 6505A Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: Good Flexibility; Medium Heat Resistance Uses: Wire and Cable Applications Wire Types: 5V-90 Agency Ratings: AS 3147-1992 Forms: Pellets Processing Method: Extru.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527-2 |
Borealis Borsoft™ SF203CF Soft Polypropylene Copolymer for Extrusion Coating Borsoft SF203CF is a new statistic-heterophasic propylene-ethylene copolymer suitable for coating applications. Its polymer structure permits perfect adhesion to certain products. According to the.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | |
Trelleborg R547 Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Trelleborg Horda Cable E8502 Strippable Semiconductive Shielding E8502 is a vulcanizing, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes.E8502 meets the requirements as bel.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Eastman Eastman AP005 Copolyester Applications:Automotive componentsBreathable filmsElectrical/electronic componentsFilm ModificationFlexible hingesHose mandrelIndustrial componentsIndustrial hoses/beltsOffice furniturePackagingPoly.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
Eurostar Starflam MX05075 PP, Flame Retardant, Injection Molding Starflam MX05075 is an Unfilled Halogen Free Flame Retardant PP Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | |
BASF Novolen® 2900 H Polypropylene Injection molded and thermoformed parts.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 14.0 MPa @Temperature 120 °C |
2030 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8350 HS PA6 (Dry) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |
|||
Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1076 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with high clarity and excellent stiffness.Applications: Film extrusion: overwrap packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (.. |
|||
Tensile Strength, Yield | 14.0 - 35.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2030 - 5080 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers. |