BASF Ultramid® 8202 L Intermediate PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202 L Intermediate PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is available in natural, heat stabilized and pigmented versions. It combines good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance.Applications: gears, fittings, casters, bearings, clips, fasteners, plugs, caps, and filter bowls.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/in³	ASTM D792
Moisture Absorption at Equilibrium	1.6 %	1.6 %	24 hour; ASTM D570
	2.7 %	2.7 %	50% RH; ASTM D570
	9.5 %	9.5 %	Saturation; ASTM D570
Linear Mold Shrinkage	0.0305 cm/cm	0.0305 in/in	1/8" Bar

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa @Temperature -40.0 °C	8700 psi @Temperature -40.0 °F	ASTM D638
Tensile Strength, Yield	21.0 MPa @Temperature 121 °C	3050 psi @Temperature 250 °F	ASTM D638
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ASTM D638
	36.0 MPa @Temperature 23.0 °C	5220 psi @Temperature 73.4 °F	ASTM D638
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	ASTM D638
Elongation at Break	>= 100 %	>= 100 %	ASTM D638
Elongation at Yield	16 % @Temperature 23.0 °C	16 % @Temperature 73.4 °F
	35 % @Temperature 80.0 °C	35 % @Temperature 176 °F
	40 % @Temperature 121 °C	40 % @Temperature 250 °F
Flexural Strength	35.0 MPa @Temperature 23.0 °C	5080 psi @Temperature 73.4 °F	ASTM D790
	155 MPa @Temperature -40.0 °C	22500 psi @Temperature -40.0 °F	ASTM D790
Flexural Modulus	0.740 GPa @Temperature 23.0 °C	107 ksi @Temperature 73.4 °F	ASTM D790
	3.66 GPa @Temperature -40.0 °C	531 ksi @Temperature -40.0 °F	ASTM D790
Izod Impact, Notched (ISO)	45.0 kJ/m² @Temperature -40.0 °C	21.4 ft-lb/in² @Temperature -40.0 °F	ASTM D256
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D3418

Processing Properties	Metric	English
Melt Temperature	240 - 285 °C	464 - 545 °F
Mold Temperature	65.0 - 80.0 °C	149 - 176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Color	Black
Commercial Status	North America