Chosun Refractories HACT-150S High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-150S High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.002943 - 0.007848 GPa @Temperature 1000 °C, Time 10800 sec |
0.4269 - 1.138 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.003924 - 0.008829 GPa @Temperature 1350 °C, Time 10800 sec |
0.5691 - 1.281 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.003924 - 0.008829 GPa @Temperature 110 °C, Time 86400 sec |
0.5691 - 1.281 ksi @Temperature 230 °F, Time 24.0 hour |
||
| Compressive Strength | 19.6 - 29.4 MPa @Temperature 1000 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 29.4 - 39.2 MPa @Temperature 1350 °C, Time 10800 sec |
4270 - 5690 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 29.4 - 39.2 MPa @Temperature 110 °C, Time 86400 sec |
4270 - 5690 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.65137 W/m-K @Temperature 260 °C |
4.5132 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.66300 W/m-K @Temperature 540 °C |
4.5938 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | limited |
| Shrinkage | -0.400 % @Temperature 1350 °C, Time 10800 sec |
-0.400 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 48 % | 48 % | |
| SiO2 | 43 % | 43 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting,Troweling | |
| Material Required for Estimating(kg/?) | 2,150 | |
| Water Required for Casting(%) | 11.5 |
Users viewing this material also viewed the following:
- Techmer ES Electrablend® PA6/6 IM C BK
- A. Schulman POLYFORT™ FPP 1640 Glass Reinforced, Mineral Fortified Homopolymer Polypropylene
- Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle
- Cossa Polimeri ESTADIENE 1030 T V0 Flame Retardant ABS
- AK Steel 420 Martensitic Stainless steel
- Ashley Polymers Ashlene® P126 PBT Polyester, 30% Glass Reinforced
- Multibase Multi-Flex® A 2504LC TPE Thermoplastic Elastomer
- Perstorp Compounds Akestra™ 100 Thermoplastic Copolyester
Copyright © lookpolymers.com All Rights Reserved