BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 6.4 % | 6.4 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 180 MPa | 26100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 8.80 GPa | 1280 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 260 MPa | 37700 psi | ASTM Test |
| Flexural Modulus | 7.59 GPa | 1100 ksi | ASTM Test |
| 8.00 GPa | 1160 ksi | ISO Data | |
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.17 mm |
1.59 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179 |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | ISO 75 |
| 297 °C | 567 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM Test |
| 250 °C | 482 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Dry Blend E7506 Polyvinyl Chloride, Rigid (PVC, Rigid)
- LyondellBasell Petrothene® NA940085 Low Density Polyethylene (Film Grade)
- LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant
- SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Tra-Con Tra-Bond 342-1 Room Temperature Cure Epoxy Adhesive
- Hexcel® HexWeb® HRP/F50 - 3.5 Nonmetallic Flex-Core Honeycomb
- CTC X-PRO TF 1020 GP Polypropylene Homopolymer, 20% Talc Filled
- Proto3000 PC-ABS Fused Deposition Modeling Polymer
- Radici Heraflex® E 6521 TPC-ET Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved