BASF Ultramid® 1310-11 NF2001 PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1310-11 NF2001 PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50mm/min; ISO 527 |
| 94.0 MPa | 13600 psi | 2 in/min; ASTM Test | |
| Elongation at Break | 20 % | 20 % | 50mm/min, Nominal strain; ISO 527 |
| 35 % | 35 % | 2 in/min; ASTM Test | |
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 123 MPa | 17800 psi | ASTM Test |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO Data |
| 3.24 GPa | 470 ksi | ASTM Test | |
| Izod Impact, Notched | 0.480 J/cm @Thickness 3.17 mm |
0.899 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 4.70 kJ/m² | 2.24 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.490 J/cm² | 2.33 ft-lb/in² | ISO 179 |
| 0.380 J/cm² @Temperature -30.0 °C |
1.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| 243 °C | 469 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| 88.0 °C | 190 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Petromont 4101 High Density Polyethylene Resin
- Dielectric Polymers NT-4502 Protective Film (discontinued **)
- Lehmann & Voss LUVOCOM® 1106-8124 Polyether imide, lubricant modified
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; over 25 to 51 mm Thickness (UNS C17200)
- Solvay Specialty Polymers Veradel® 3300 PREM Polyethersulfone (PESU)
- Polyplastics Duranex® CTN7133 Polybutylene Terephthalate (PBT), Higher comparative tracking index, FR, GF filled
- Eurostar Starpylen MF004S PP, 20% Glass Fiber Filled, Injection Molded
- Asahi Glass Fluon® AH-2000 LM-ETFE, Non-Conductive Type, Fluororesin
- Cosmic Plastics D33 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved