3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Applied warm and can bond a variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and to glass.Information provided by 3M
Physical Properties Metric English Comments
Density >= 1.08 g/cc
>= 0.0390 lb/in³
Brookfield Viscosity 16000 cP
16000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 47
47
Tensile Strength at Break 22.1 MPa
3210 psi
ASTM D638 Die C
Elongation at Break 600 %
600 %
ASTM D638 Die C
Tensile Modulus 0.0228 GPa
3.30 ksi
ASMT D638 Die C
Shear Strength 0.276 MPa

@Temperature 82.0 °C
40.0 psi

@Temperature 180 °F
Overlap, FRP
0.414 MPa

@Temperature 82.0 °C
60.0 psi

@Temperature 180 °F
Overlap, Maple
3.59 MPa

@Temperature 23.0 °C
520 psi

@Temperature 73.4 °F
Overlap, Polystyrene
6.07 MPa

@Temperature 23.0 °C
880 psi

@Temperature 73.4 °F
Overlap, ABS, Substrate Failure
6.89 MPa

@Temperature 23.0 °C
1000 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
7.93 MPa

@Temperature 23.0 °C
1150 psi

@Temperature 73.4 °F
Overlap, Polyacrylic
9.58 MPa

@Temperature 23.0 °C
1390 psi

@Temperature 73.4 °F
Overlap, Maple
10.1 MPa

@Temperature 23.0 °C
1470 psi

@Temperature 73.4 °F
Overlap, PVC, Substrate Failure
11.7 MPa

@Temperature 23.0 °C
1690 psi

@Temperature 73.4 °F
Overlap, FRP
Peel Strength 0.175 kN/m
1.00 pli
180°, Polystyrene
3.68 kN/m
21.0 pli
T-Peel, Initial, Substrate failure
4.38 kN/m
25.0 pli
T-Peel, Aged 71°C for 2 weeks, Substrate failure
9.47 kN/m
54.0 pli
180°, Polyacrylic
10.9 kN/m
62.0 pli
180°, ABS
12.6 kN/m
72.0 pli
180°, Aluminum
14.2 kN/m
81.0 pli
180°, Glass
15.3 kN/m
87.0 pli
180°, Polycarbonate, Cotton duck failed during testing
16.1 kN/m
92.0 pli
180°, PVC, Cotton duck failed during testing
16.7 kN/m
95.0 pli
180°, FRP, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 1.00 min
0.0167 hour
Set Time