BASF Ultraform N 2320 U03 UNC Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform N
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform N 2320 U03 UNC Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform N2320 U03 UNC Q600 is a rapidly freezing UV stabilized general-purpose injection molding grade.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.020 cm/cm
0.020 in/in
ASTM Data; MD
Linear Mold Shrinkage, Flow 0.021 cm/cm
0.021 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ISO Data
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 63.0 MPa
9140 psi
50mm/min; ISO 527
63.0 MPa
9140 psi
2 in/min; ASTM Test
33.0 MPa

@Temperature 80.0 °C
4790 psi

@Temperature 176 °F
ISO Data
93.0 MPa

@Temperature -40.0 °C
13500 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break 30 %
30 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 9.4 %
9.4 %
50mm/min; ISO 527
9.4 %
9.4 %
2 in/min; ASTM Test
5.8 %

@Temperature -40.0 °C
5.8 %

@Temperature -40.0 °F
ISO Data
9.3 %

@Temperature 80.0 °C
9.3 %

@Temperature 176 °F
ISO Data
Tensile Modulus 2.60 GPa
377 ksi
1mm/min; ISO 527
2.76 GPa
400 ksi
ASTM Test
Flexural Modulus 4.00 GPa
580 ksi
ISO Data
Izod Impact, Notched 0.598 J/cm

@Temperature -40.0 °C
1.12 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.694 J/cm

@Thickness 3.17 mm
1.30 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
ISO Test
Charpy Impact Unnotched 20.0 J/cm²
95.2 ft-lb/in²
ISO 179
18.0 J/cm²

@Temperature -30.0 °C
85.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Tensile Creep Modulus, 1 hour 1800 MPa
261000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 1400 MPa
203000 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
33.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359
Melting Point 166 °C
331 °F
10 K/min
166 °C
331 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 156 °C
313 °F
ISO 75
160 °C
320 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75
110 °C
230 °F
ASTM Test
Vicat Softening Point 150 °C
302 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding