BASF Ultradur® B 4406 G2 10% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur® B 4406 G2 10% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a PBT, flame-retardant injection-molding grades, with 10% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and lighting components.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH |
| Viscosity Measurement | 120 | 120 | [ml/g]; Viscosity number; ISO 1628 |
| 70 @Temperature 290 °C |
70 @Temperature 554 °F |
20 mins plasticating | |
| 75 @Temperature 280 °C |
75 @Temperature 536 °F |
30 mins plasticating | |
| 75 @Temperature 300 °C |
75 @Temperature 572 °F |
10 mins plasticating | |
| 90 @Temperature 270 °C |
90 @Temperature 518 °F |
30 mins plasticating | |
| 95 @Temperature 290 °C |
95 @Temperature 554 °F |
10 mins plasticating | |
| 100 @Temperature 300 °C |
100 @Temperature 572 °F |
5 mins plasticating | |
| 100 @Temperature 260 °C |
100 @Temperature 500 °F |
30 mins plasticating | |
| 105 @Temperature 280 °C |
105 @Temperature 536 °F |
10 mins plasticating | |
| 106 @Temperature 250 °C |
106 @Temperature 482 °F |
30 mins plasticating | |
| 110 @Temperature 270 °C |
110 @Temperature 518 °F |
10 mins plasticating | |
| 115 @Temperature 260 °C |
115 @Temperature 500 °F |
10 mins plasticating | |
| 115 @Temperature 240 °C |
115 @Temperature 464 °F |
30 mins plasticating | |
| 117 @Temperature 250 °C |
117 @Temperature 482 °F |
10 mins plasticating | |
| 120 @Temperature 240 °C |
120 @Temperature 464 °F |
10 mins plasticating | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | Sheet |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Sheet |
| Melt Flow | 22.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
22.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 3.3 % | 3.3 % | 50mm/min; ISO 527-2 |
| Modulus of Elasticity | 5.50 GPa | 798 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | W<sub>501</sub> housing; ISO 6603-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | IEC 1006 |
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 |
| 130 °C | 266 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |
| 210 °C | 410 °F | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-2 |
| Decomposition Temperature | >= 290 °C | >= 554 °F | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243/1 |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 250 | |
| Comparative Tracking Index | 150 V | 150 V | Test solution B; IEC 112 |
| 225 V | 225 V | Test solution A; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 240 °C | 464 °F | Feeding zone |
| Zone 2 | 245 °C | 473 °F | Compression |
| Zone 3 | 250 °C | 482 °F | Metering-zone |
| Zone 4 | 250 °C | 482 °F | Nozzle |
| Melt Temperature | 250 °C | 482 °F | Optimal |
| 260 °C | 500 °F | for shrinkage test | |
| 250 - 275 °C | 482 - 527 °F | Injection-molding | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| 80.0 °C | 176 °F | for shrinkage test, Optimal | |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural, Colored, Black and Special Colors | |
| Commercial Status | Europe | |
| Ignition Temperature | >350°C | ASTM D1929 |
| Peripheral screw speed | <0.25 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs PT465 K2PtCl6 Potassium hexachloroplatinate(IV)
- LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement (discontinued **)
- Kazanorgsintez E-17 Petroleum Resin
- LyondellBasell Aquathene® CM04482 Catalyst Masterbatch
- Sharadaa Ceramics LI SILL-II High Alumina Brick
- A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene
- Hexcel® HexWeb® CR-PAA™ 3/8-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- DuPont Performance Polymers Zytel® RS LC1610 BK387 Nylon 1010 (Unverified Data**)
- Arlon 10502R010 0.010" (.254 mm) Cured/Post-Cured Unsupported Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved