BASF Ultradur® B 4300 M5 25% Mineral Filled PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled
Manufacturer	BASF
Trade Name	Ultradur®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultradur® B 4300 M5 25% Mineral Filled PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Is a PBT-HI, injection-molding grade reinforced with 25% of minerals, for the production of parts with good surface quality and low warpage, e.g. housings and visible parts of domestic appliances.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.600 - 0.900 g/cc	0.0217 - 0.0325 lb/in³
Density	1.51 g/cc	0.0546 lb/in³	ISO 1183
Water Absorption	0.40 %	0.40 %	Saturation; DIN 53495/1L
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C; 50% RH
Viscosity Measurement	117	117	[ml/g]; Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow	0.0174 cm/cm	0.0174 in/in	Sheet
	0.018 cm/cm	0.018 in/in	60x60x2 mm; ISO 294
Linear Mold Shrinkage, Transverse	0.0168 cm/cm	0.0168 in/in	60x60x2 mm; ISO 294
	0.0178 cm/cm	0.0178 in/in	Sheet
Melt Flow	18.12 g/10 min @Load 2.16 kg, Temperature 250 °C	18.12 g/10 min @Load 4.76 lb, Temperature 482 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	170 MPa	24700 psi	ISO 2039-1
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ISO 527-2
Elongation at Break	4.5 %	4.5 %	50mm/min; ISO 527-2
Elongation at Yield	3.0 %	3.0 %	50 mm/min; ISO 527-2
Modulus of Elasticity	4.00 GPa	580 ksi	ISO 527-2
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm²	1.90 ft-lb/in²	ISO 179/1eA
Dart Drop, Total Energy	20.0 J	14.8 ft-lb	W<sub>501</sub> housing; ISO 6603-1
Tensile Creep Modulus, 1000 hours	2000 MPa @Strain <=0.500 %	290000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	7.00 - 11.0 µm/m-°C @Temperature 23.0 - 80.0 °C	3.89 - 6.11 µin/in-°F @Temperature 73.4 - 176 °F	DIN 53752
Specific Heat Capacity	1.50 J/g-°C	0.359 BTU/lb-°F	IEC 1006
Melting Point	220 - 225 °C	428 - 437 °F	DSC; ISO 11357-3
Maximum Service Temperature, Air	120 °C	248 °F	at 50% loss of tensile strength after 20000h; IEC 216-1
	130 °C	266 °F	at 50% loss of tensile strength after 5000h; IEC 216-1
	200 °C	392 °F
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F	ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C	194 °F	ISO 75-2
Decomposition Temperature	>= 290 °C	>= 554 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Diameter 0.800 mm	HB @Diameter 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 93
Dielectric Constant	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	IEC 250
	3.6 @Frequency 100 Hz	3.6 @Frequency 100 Hz	IEC 250
Dielectric Strength	100 kV/mm	2540 kV/in	IEC 243/1
Dissipation Factor	0.0012 @Frequency 100 Hz	0.0012 @Frequency 100 Hz	IEC 250
	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 250
Comparative Tracking Index	150 V	150 V	Test solution B; IEC 112
	225 V	225 V	Test solution A; IEC 112

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	for shrinkage test, Optimal
	250 - 275 °C	482 - 527 °F	Injection-molding
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F	Injection molding
	60.0 °C	140 °F	for shrinkage test, Optimal

Descriptive Properties	Value	Comments
Color	Natural, Colored, Black and Special Colors
Commercial Status	Europe
Ignition Temperature	350°C	ASTM D1929
Primary Processing Technique	Injection Molding