BASF Ultradur® B 4300 G6 LT 30% Glass Filled BK 150926 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® B 4300 G6 LT 30% Glass Filled BK 150926 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Easy flowing injection molding grade with 30 % glass fibers; for rigid, tough and dimensionally stable technical parts (eg windshield wiper arms, printed circuit boards PCBs), housing, consoles, contact carriers, covers)Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.600 - 0.900 g/cc
0.0217 - 0.0325 lb/in³
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62
Viscosity Measurement 102
102
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0034 cm/cm
0.0034 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0107 cm/cm
0.0107 in/in
ISO 2577
0.011 cm/cm
0.011 in/in
plate with film gate 150x150x3mm<sup>3</sup>
Melt Flow 16.83 g/10 min

@Load 2.16 kg,
Temperature 250 °C
16.83 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 190 MPa

@Load 98.0 kg,
Time 30.0 sec
27600 psi

@Load 216 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 9.80 GPa
1420 ksi
ISO 527-1/-2
Flexural Strength 200 MPa
29000 psi
ISO 178
Charpy Impact Unnotched 7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.950 J/cm²

@Temperature 23.0 °C
4.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 7500 MPa

@Strain <=0.500 %
1.09e+6 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 - 30.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
11.1 - 16.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
DIN 52612-1
Melting Point 223 °C
433 °F
ISO 11357-1/-2
Maximum Service Temperature, Air 140 °C
284 °F
at 50% loss of tensile strength after 20,000hr
160 °C
320 °F
at 50% loss of tensile strength after 5,000hr
210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/-2
Decomposition Temperature >= 290 °C
>= 554 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Diameter 4.00 mm
HB

@Diameter 0.157 in
HB

@Diameter 0.400 mm
HB

@Diameter 0.0157 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0025

@Frequency 100 Hz
0.0025

@Frequency 100 Hz
IEC 60250
0.017

@Frequency 1.00e+6 Hz
0.017

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
Test Solution B; IEC 60112
375 V
375 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection molding/Extrusion
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection molding
Descriptive Properties Value Comments
Color BK 15092
Commercial Status Europe
Ignition Temperature 350°C
ASTM D1929