BASF Polystyrol® 454 C Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 454 C Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowing, medium-impact grade.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 200 °C |
13 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | 40 % | 40 % | |
| Elongation at Yield | 1.4 % | 1.4 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 12.0 J/cm² | 57.1 ft-lb/in² | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Tensile Creep Modulus, 1000 hours | 1700 MPa | 247000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Vicat Softening Point | 84.0 °C | 183 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00015 @Frequency 100 Hz |
0.00015 @Frequency 100 Hz |
|
| 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 350 V | 350 V |
Users viewing this material also viewed the following:
- MV Labs AU450 NH4AuCl4·xH2O Ammonium tetrachloroaurate(III) hydrate
- Grupo Repol Dinalon® B1X25 G30W PA6 30% Glass Fiber, Reduced Water Abs.
- SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific)
- A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene
- ExxonMobil Vacmul 3 A
- Loctite® 352 Acrylic Light Cure Adhesive
- Eurostar Starflam PX07037 PA6, Flame Retardant, Injection Molded
- Axiall 22905 Coax & Telecom Flexible PVC
- A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer
Copyright © lookpolymers.com All Rights Reserved