PolyOne Lubri-Tech™ MP-000/10T Modified PPO - 10% PTFE  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, PTFE Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ MP-000/10T Modified PPO - 10% PTFE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 3.17 mm
 0.0040 - 0.0060 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 52.0 MPa
7540 psi
ASTM D638
Elongation at Break 2.0 - 5.0 %
2.0 - 5.0 %
ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
ASTM D638
Flexural Yield Strength 79.0 MPa
11500 psi
ASTM D790
Flexural Modulus 2.59 GPa
376 ksi
ASTM D790
Izod Impact, Notched 0.590 - 0.960 J/cm

@Thickness 6.35 mm
 1.11 - 1.80 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 601 °F
Stock
Mold Temperature 107 - 121 °C
225 - 250 °F
Drying Temperature 121 °C
250 °F