BASF Capron® 5233G HS BK-102 33% Glass-Filled Nylon 66 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 5233G HS BK-102 33% Glass-Filled Nylon 66 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 5233G HS BK-102 is a 35% glass reinforced, heat stabilized, pigmented black nylon 6,6 injection molding compound offering excellent strength, rigidity, stiffness, creep resistance, and dimensional stability. This balance of engineering properties combined with excellent processability makes it ideal in applications replacing metal. It maintains excellent chemical resistance to greases, oils and hydrocarbons. It is also available in natural and pigmented versions.Capron 5233G HS BK-102 is generally recommended for applications such as window locks, valve bodies, door and window hardware, connectors, switch components, relay parts, terminal blocks, power tool components, gears and automotive housings.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 290-315 degC (555-600 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95degC (176-203 degF) is recommended, but temperatures of as low as 45 degC (113degF) and as high as 105 degC (221 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.187 g/cc
0.04288 lb/in³
Melt Density
1.39 g/cc
0.0502 lb/in³
ISO data
Water Absorption 0.80 %
0.80 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 1.6 %
1.6 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 5.6 %
5.6 %
in water; 23°C; ISO data
Viscosity Measurement 59
59
Formic Acid Viscosity; ISO data
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM and ISO value
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 200 MPa
29000 psi
ASTM value at 5mm/min.
202 MPa
29300 psi
ISO value at 5mm/min.
Elongation at Break 3.0 %
3.0 %
ISO, 5 mm/minl
3.0 %
3.0 %
ASTM, 5 mm/minl
Tensile Modulus 10.4 GPa
1510 ksi
ISO test
Flexural Modulus 8.80 GPa
1280 ksi
ISO Value
9.69 GPa
1410 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Shear Modulus 3.90 GPa
566 ksi
calculated
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C

@Temperature 20.0 °C
12.8 µin/in-°F

@Temperature 68.0 °F
ISO data
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO data
Specific Heat Capacity 2.35 J/g-°C
0.562 BTU/lb-°F
Melt value
Thermal Conductivity 0.331 W/m-K
2.30 BTU-in/hr-ft²-°F
Melt
Melting Point 260 °C
500 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ISO data
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO data
251 °C
484 °F
ASTM Data
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Dielectric Strength 30.0 kV/mm
762 kV/in
ISO data
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
See Materials Notes
Mold Temperature 80.0 °C
176 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes