Azoty Tarnow™ Tarnamid® T-29 MCS Polyamide 6 - Colored

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	Azoty Tarnow™ (Zaklady Azotowe)
Trade Name	Tarnamid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azoty Tarnow™ Tarnamid® T-29 MCS Polyamide 6 - Colored.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Colored medium-high viscosity grade for injection molding.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capacityGood fatigue strengthVery good sliding properties, abrasion resistance, low coefficient of frictionHigh thermal resistance, admissible temperature of continuous operation from -60°C to +150°CHigh chemical resistance, particularly to organic solvents, oils, lubricants and fuelsConsiderable moisture absorption influencing mechanical and electrical propertiesSelf-extinguishing properties (fire retardant properties)Good electro-insulating propertiesGood optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendmentsInformation provided by Azoty Tarnow™.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ISO 1183
Water Absorption	1.8 % @Time 86400 sec	1.8 % @Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.016 cm/cm	0.016 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.018 cm/cm	0.018 in/in	ISO 294-4
Melt Flow	45 g/10 min @Load 5.00 kg, Temperature 275 °C	45 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	75.0 MPa @Load 36.5 kg	10900 psi @Load 80.5 lb	cond.; ISO 2039-1
	140 MPa @Load 36.5 kg	20300 psi @Load 80.5 lb	dry; ISO 2039-1
Tensile Strength, Yield	45.0 MPa	6530 psi	cond.; ISO 527
	75.0 MPa	10900 psi	dry; ISO 527
Elongation at Break	50 %	50 %	dry; ISO 527
	200 %	200 %	cond.; ISO 527
Tensile Modulus	1.10 GPa	160 ksi	cond.; ISO 527
	3.00 GPa	435 ksi	dry; ISO 527
Flexural Strength	28.0 MPa	4060 psi	cond.; ISO 178
	85.0 MPa	12300 psi	dry; ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179 1eU
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²	dry; ISO 179 1eA
	NB	NB	cond.; ISO 179 1eA

Thermal Properties	Metric	English	Comments
Melting Point	221 °C	430 °F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	cond.; ISO 75
	60.0 °C	140 °F	dry; ISO 75
Vicat Softening Point	190 °C @Load 5.10 kg	374 °F @Load 11.2 lb	ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Glow Wire Test	750 °C @Thickness 2.00 mm	1380 °F @Thickness 0.0787 in	PN-EN-60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	cond.; IEC 93
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	dry; IEC 93
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	cond.; IEC 93
	1.00e+15 ohm	1.00e+15 ohm	dry; IEC 93
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 243-1
Comparative Tracking Index	600 V	600 V	IEC 112

Processing Properties	Metric	English	Comments
Melt Temperature	230 - 290 °C	446 - 554 °F
Mold Temperature	60.0 - 120 °C	140 - 248 °F	80 - 90°C is recommended
Drying Temperature	75.0 - 100 °C @Time 7200 - 14400 sec	167 - 212 °F @Time 2.00 - 4.00 hour
Moisture Content	<= 0.10 %	<= 0.10 %
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended

Users viewing this material also viewed the following: