Azoty Tarnow™ TARNOFORM 200 HI4 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 200 HI4 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rubber modified grade with very high impact strength and damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Melt Flow | 2.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ISO 2039-2 |
| Ball Indentation Hardness | 82.0 MPa | 11900 psi | 358 N; ISO 2039-1 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 51 % | 51 % | ISO 527 |
| Flexural Strength | 36.0 MPa | 5220 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact Unnotched | NB | NB | 1 eU, 15 J; ISO 179 |
| Charpy Impact, Notched | 2.80 J/cm² | 13.3 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.48 J/g-°C | 0.354 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75 |
| Vicat Softening Point | 121 °C | 250 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz |
4.3 @Frequency 1e+6 Hz |
IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243 |
| Dissipation Factor | 0.034 @Frequency 1e+6 Hz |
0.034 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 60.0 - 120 °C | 140 - 248 °F | Barrel temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® FD 20 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
- Hybrid Plastics POSS® MA0747 TrisMethacrylCyclohexyl-POSS®
- LG Chemical LUMID GP2130B(W) PA66+GF13%, General Purpose
- Techmer ES HiFill® PA6/6 GF60 HS L BK 60% Glass Filled
- Stir SpA AF 95 CZ (PVC)
- Samsung Cheil Industries Starex® WR-9120 ASA, Unreinforced
- Teknor Apex HFFR 2003 Polyolefin, Halogen Free
- Formosa Plastics Formolene® HB6007 Blow Molding HDPE
- ExxonMobil Santoprene® 201-87 Thermoplastic Elastomer
- Dow Nordel® IP 5565 Heat Resistant Peroxide Cured
Copyright © lookpolymers.com All Rights Reserved