Asia International Enterprise (Hong Kong) 60G3F Nylon 66, 15% Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 60G3F Nylon 66, 15% Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc @Temperature 23.0 °C |
1.35 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 108 MPa | 15600 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 177 MPa | 25700 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Pyrotek TS-101 Thermoset Electrical Insulation Product (Nema Grade: C)
- SABIC Innovative Plastics Lexan® 123R PC
- Techmer ES HiFill® PA6 LE BK (Dry)
- SABIC Innovative Plastics Xenoy® CL101 PBT+PC
- Techmer ES Plastiblend® PA6 GF20 RM BK Nylon 6
- Trimay® Wear Plate TWP57 Chromium-based Flux Cored Weld Wire & Electrode
- Chosun Refractories HSC-15G Dense and High-Strength Castable, Credens
- Asahi Kasei Leona® FG173 Nylon 66
- BCC Products BC 7062-3H Epoxy Casting
Copyright © lookpolymers.com All Rights Reserved