- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1239H is a 30% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FL933 PC
- Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified
- SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI
- Total PPC 7652 Polypropylene, Heterophasic Copolymer, Injection Molding
- Tra-Con Tra-Coat TC2 UV Cure Screen Printable Adhesive
- Formosa Plastics Formolon® 685 PVC
- Cheng Yu Plastic A779 Lubrication ABS
- 3M 3635-0171 Diffuser Film
- Fainplast Compounds PM 83/M Flexible PVC, Extrusion
- PolyOne Lubri-Tech™ AM-30CF/15T Polyphthalamide (PPA), Carbon Fiber Reinforced, PTFE Lubricated (discontinued
Copyright © lookpolymers.com All Rights Reserved