Asahi Kasei Xyron® X5402 PPE/PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® X5402 PPE/PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Oil ResistantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.400 % | 0.400 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 0.980 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 1.20 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.25 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
50% RH; ASTM D150 |
| 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dissipation Factor | 0.0040 @Frequency 60 Hz |
0.0040 @Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
50% RH; ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 300 °C | 500 - 572 °F | Resin Temperature |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY6009 PC+ABS (Asia Pacific)
- SABIC Innovative Plastics Lexan® 141R PC (Europe-Africa-Middle East)
- Pau Tai UNISTAB BC-505 Liquid Barium-Cadmium-Zinc Stabilizer
- Karina CAK 75-48/1 Black PVC Compound
- Kuraray SEPTON® A3 Hot Melt Adhesive
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR MBTS
- DAK Americas Laser+® 7000 (C91A) PET
- Adell RQ-16 Copolymer Polypropylene, 30% Mica Reinforced
- BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved