- Honeywell ACLAR® UltRx 3000 CTFE Homopolymer, Barrier Film
Honeywell ACLAR® UltRx 3000 CTFE Homopolymer, Barrier Film
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Honeywell |
| Trade Name | ACLAR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® UltRx 3000 CTFE Homopolymer, Barrier Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® UltRx 3000 is a 3 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.10 g/cc | 0.0760 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0120 g/m²/day | 0.000773 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.0230 g/m²/day | 0.00148 g/100 in²/day | 86°F (30°C) / 65% RH; ASTM F1249 | |
| 0.0250 g/m²/day | 0.00161 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.0620 g/m²/day | 0.00399 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| 0.0880 g/m²/day | 0.00567 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| Thickness | 76.2 microns | 3.00 mil | |
| Surface Tension | >= 42 dynes/cm | >= 42 dynes/cm | ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 150 - 225 % | 150 - 225 % | ASTM D882 |
| Film Elongation at Break, TD | 175 - 225 % | 175 - 225 % | ASTM D882 |
| Secant Modulus, MD | 1.103 - 1.38 GPa | 160.0 - 200 ksi | ASTM D882 |
| Secant Modulus, TD | 1.103 - 1.38 GPa | 160.0 - 200 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 41.4 - 62.1 MPa | 6000 - 9000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.6 - 48.3 MPa | 4000 - 7000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Shrinkage, MD | <= 6.0 % | <= 6.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= -6.0 % | <= -6.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 40 PBT reinforced with 40% glass fibre
- SABIC Innovative Plastics Lexan® DMX2415 PC
- LyondellBasell Petrothene® NA814000 Low Density Polyethylene
- Techmer ES HiFill® PA6/6 GF18 FR BK 18% Glass Filled
- Teknor Apex Beetle® MD21 Nylon 6, Extrusion Grade
- The Chemical Company Nature-Flexx 509 Acetyl Tributyl Citrate, C20H34O8
- E-Polymers SEPAZ® V220A 20% Glass Fiber Reinforced PPA
- Arkema Group Pebax® 6333 SA 01 Polyether Block Amide (PEBA)
- BCC Products MB 1200 Polyurethane Foam Modeling Board
- Pasargad Polymer Peyvand Pasamid 3P-M2000W Nylon 66
Copyright © lookpolymers.com All Rights Reserved