Asahi Kasei Tenac®-C EX351 Acetal Copolymer, Extrusion Grade (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac®-C EX351 Acetal Copolymer, Extrusion Grade
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-viscosity grade amenable to extrusion.Applications: Extruded rods and sheets.This product is not a part of the standard product line dated 2003.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | Asahi Chemical test |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | melt index; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 60.8 MPa | 8820 psi | 5 mm/min; parallel to flow; ASTM D638 |
| Elongation at Break | 75 % | 75 % | 5 mm/min; parallel to flow; ASTM D638 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 14 | 14 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 200 °C | 356 - 392 °F | Resin temp |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1100L-xx93FRSD Polyvinyl Chloride, Flexible (PVC, Flexible)
- Rogers Corporation Poron® 4790-92-12 P Series Urethane Foam, Extra Soft, Slow Rebound, PET Film Reinforced
- Pacific Sintered Materials BT-121-R Bronze Powdered Metal
- Freudenberg Simrit V169 Fluoroelastomer Self-Lube
- Monmouth Rubber & Plastics Durafoamâ„¢ C43NBR Nitrile Rubber
- Multibase Dow Corning® MB50-011 Siloxane Additive
- SABIC Innovative Plastics LNP Thermocomp MX06050 PP (Europe-Africa-Middle East)
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- Eastman Eastar MN059 Copolyester
- CP-Polymer-Technik Wellamid® 6000 GS 25 HWCP 25% Glass Sphere Filled Nylon 6, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved