Asahi Kasei Leona® FR200 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Asahi Kasei |
| Trade Name | Leona® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Leona® FR200 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UL94 V-0; halogen-free and phosphor-free.Applications:Connectors, switches, and other electrical and electronic parts Information provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | Dry; ASTM D792 |
| Water Absorption | 2.4 % | 2.4 % | Wet |
| Linear Mold Shrinkage | 0.013 - 0.020 cm/cm | 0.013 - 0.020 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | Dry; ASTM D785 |
| Hardness, Rockwell R | 90 | 90 | Wet; ASTM D785 |
| 118 | 118 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Wet; ASTM D638 |
| 79.0 MPa | 11500 psi | Dry; ASTM D638 | |
| Elongation at Break | 25 % | 25 % | Dry; ASTM D638 |
| 80 % | 80 % | Wet; ASTM D638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | Wet; ASTM D790 |
| 118 MPa | 17100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.10 GPa | 160 ksi | Wet; ASTM D790 |
| 2.90 GPa | 421 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | Dry; ASTM D256 |
| 1.18 J/cm | 2.21 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
Dry; ASTM D696 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Dry |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Dry; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | Dry |
| Oxygen Index | 32 % | 32 % | Dry; ASTM D2863 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Polymist® F-5 PTFE Powder Lubricant (discontinued **)
- Sharadaa Ceramics REFCAST LC95 Low Cement Castables
- DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer
- Zeon Chemicals Quintone® D100 Aliphatic Hydrocarbon Resin
- Dow Corning 8500 Conditioning Agents
- Alliance N-42SH Neodymium Iron Boron Magnetic Material
- Arkema Group Rilsan® AESN P302 TL Nylon 12, Flexible Tubing Grade (Dry)
- Ascend Performance Materials Vydyne® 50BW Nylon 66, General Purpose
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 1.5 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved