SABIC Innovative Plastics LNP THERMOCOMP TF006 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TF006 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.360 % | 0.360 % | 50% RH, 24 hrs; ASTM D570 |
| 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 16 % | 16 % | Type I, 5 mm/min; ASTM D638 |
| 16 % | 16 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 15.5 % | 15.5 % | 5 mm/min; ISO 527 |
| 16.3 % | 16.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.48 GPa | 215 ksi | 50 mm/min; ASTM D638 |
| 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 58.0 MPa | 8410 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.69 GPa | 245 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 5.12 J/cm | 9.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | NB1751; ASTM D4812 |
| Izod Impact, Notched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 131 kJ/m² | 62.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 19.0 J | 14.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 17.0 J | 12.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 130 µm/m-°C @Temperature -40.0 - 40.0 °C |
72.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 131 µm/m-°C @Temperature -40.0 - 40.0 °C |
72.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 167 °C @Thickness 3.20 mm |
333 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pyrotek L-8 Fiberseal Blanket
- Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant
- MetalTek C86300 High Tensile Manganese Bronze
- Lucite International Colacryl ® TS1742 Acrylic Dental Resin
- Solvay Specialty Polymers Ixef® BXT 2000-0203 Polyarylamide (PARA)
- Epoxy Technology EPO-TEK® 301-2 Optically Transparent Epoxy
- BNZ Materials BNZ-26 Insulating Firebrick
- Beijing Chemical Industry KAIFA® 304-G30 PBT Resin
- BASF Neopolen® P 9435 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- LATI Latilub 88/10-15T K/30 PEEK, 30% Carbon Fiber Reinforced, PTFE Filled
Copyright © lookpolymers.com All Rights Reserved