PolyOne Stat-Tech™ AT-000/000 ESD Acetal-Copolymer (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AT-000/000 ESD Acetal-Copolymer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:AntistaticInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Thickness 3.17 mm |
0.010 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.6 MPa | 6900 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® EX58F ABS (Asia Pacific)
- Lord Adhesives Fusor® 2001 / 2002 Urethane Adhesive
- Solvay MACKADET® CA-ND Surfactant
- Borealis Borcoat™ BB125E Polypropylene Adhesive for Steel Pipe Coating
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 80A, Non-Black Peroxide Cure
- Dow Corning XIAMETER® PMCPMEM-0346 Emulsion
- Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler
- LATI Latiohm 75/4-03 PD01 G/20 PBT, 20% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved