Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Top layer of side 2: alloy 600 foil; Bottom layer of side 2: cured silicone rubber; Substrate is 7628 fiberglass; Side 1: cured silicone rubber
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | silicone property (alloy 600 = 8.41 g/cc); Arlon SQA-TMS-024 |
| Thickness | 25.4 microns | 1.00 mil | laminated foil; Arlon SQA-TMS-003 |
| 50.8 microns | 2.00 mil | side 1; Arlon SQA-TMS-003 | |
| 140 microns | 5.50 mil | side 2; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |
| 419 microns | 16.5 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 45 | 45 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 6.21 MPa | 900 psi | silicone property; ASTM D412 |
| Elongation at Break | 400 % | 400 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0483 MPa | 7.00 psi | bond to alloy 600; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 °C |
7.72 µin/in-°F @Temperature 68.0 °F |
alloy 600 property |
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | silicone property; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
|
| Shelf Life | 12.0 Month @Temperature 21.1 °C |
12.0 Month @Temperature 70.0 °F |
Users viewing this material also viewed the following:
- Nye Lubricants PML-81 Oil
- Niagara LaSalle 4140 Leaded Cold Finished Steel Bar
- SABIC Innovative Plastics FL405 PC
- Pau Tai B-502, Special Lubricants
- NOVA Chemicals Sclair® 97B HDPE Extrusion Resin (discontinued **)
- Styron CALIBREâ„¢ 280-25 Polycarbonate
- Hexcel® HexPly® F263 Epoxy Resin, F3T584 Carbon Fabric
- Trelleborg R396 Commercial Natural Rubber Polyisoprene
- Diamond Polymers Centrex® 835 Sheet Extrusion Grade
- Bhansali Engineering Abstron AN-450 Flame Retardant ABS Grade
Copyright © lookpolymers.com All Rights Reserved