Arlon 51146R020 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51146R020 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 76.2 microns | 3.00 mil | side 1 silicone; Arlon SQA-TMS-003 |
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |
| 229 microns | 9.00 mil | side 2 silicone; Arlon SQA-TMS-003 | |
| 508 microns | 20.0 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
| Elongation at Break | 225 % | 225 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0586 MPa | 8.50 psi | Arlon SQA-TMS-011 |
| Tear Strength | 15.8 kN/m | 90.0 pli | silicone property; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 200 °C | 392 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 HH-GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced
- SABIC Innovative Plastics Lexan® ML6413 PC (Asia Pacific)
- Solvay Specialty Polymers KetaSpire® KT-880 GF30 Polyetheretherketone (PEEK) (Unverified Data**)
- Overview of materials for Nylon 66, 40% Mineral Filled
- Fine Organics FINALUX G 114 Lubricant Additive
- Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F)
- Shinil Chemical SHINFLAME PBT GF Flame Retardant Polymer Lamp Housing
- ExxonMobil Teresstic 320
- Oceanchem Group Magnesium Hydroxide
- Lubrizol ESTANE® 58206 Ester Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved