BASF Polystyrol® 445 E WU Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 445 E WU Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowing, heat-resistant, medium-impact, flame-retardant grade. Application example: electrical distribution boxes.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Water Absorption | 0.12 % | 0.12 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 200 °C |
13 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
| Elongation at Break | 30 % | 30 % | |
| Elongation at Yield | 1.6 % | 1.6 % | |
| Tensile Modulus | 2.45 GPa | 355 ksi | |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
| Tensile Creep Modulus, 1000 hours | 1600 MPa | 232000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | |
| Vicat Softening Point | 87.0 °C | 189 °F | |
| Flammability, UL94 | V-2 @Thickness 3.18 mm |
V-2 @Thickness 0.125 in |
|
| Oxygen Index | 26 % | 26 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00050 @Frequency 1e+6 Hz |
0.00050 @Frequency 1e+6 Hz |
|
| 0.00060 @Frequency 100 Hz |
0.00060 @Frequency 100 Hz |
||
| Comparative Tracking Index | 400 V | 400 V |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6812 Adhesive
- Solvay ALKAMULS® 696 Surfactant
- Teknor Apex Sinvicomp SRP 4606 Polyvinyl Chloride, Rigid
- Plastics Group Polifil® 930L-33GF Glass Fiber-Reinforced Nylon 6 (DAM)
- Polyram PlusTek PA100 Nylon 6.6, General Purpose
- A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene
- Ecomass® 4703ZC87 Stainless Steel Filled Polyurethane
- DuPont Teijin Films Melinex® 377 Polyester Film, 48 Gauge
- C.O.I.M. LARIPUR® LPR2103-90AE PTMG Polyether Polyurethane
- 3M Scotchkote™ 80BG 536 Urethane Elastomer
Copyright © lookpolymers.com All Rights Reserved