- Sax Polymers SAXAMID 126F6RY01 Nylon 6, 30% Glass Fiber
Sax Polymers SAXAMID 126F6RY01 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F6RY01 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F6RY01 is a polyamide 6 injection-molding-grade reinforced with 30% glass fibers. It has a halogen-free flame retardant.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 134 MPa | 19400 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 11.2 GPa | 1620 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 6.90 J/cm² @Temperature -30.0 °C |
32.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 215 °C | 419 °F | B/120; ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 750 °C @Thickness 1.00 mm |
1380 °F @Thickness 0.0394 in |
GWIT; IEC 60695-2-13 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Victrex® ST™ STG45 PolyEtherKetoneEtherKetoneKetone, Unreinforced
- Resinlab® CYNERGY CA6102 Adhesive
- Karina E 650D35/1-C Ivory PVC Compound
- Shakespeare Resistat® F9222 B040 Nylon 6 Monofilament
- A. Schulman POLYBATCH™ Teal 30316 Concentrate Based In LLDPE
- BASF Pluracol® P410R Specialty Polyol
- BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Dry)
- Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound
- Saint-Gobain Chemfab® 5 Industrial PTFE-Coated Glass
Copyright © lookpolymers.com All Rights Reserved