ExxonMobil Oppalyte™ 52MH647 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Oppalyte™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Oppalyte™ 52MH647 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strengths even under low pressure sealingGood aroma barrierExcellent packaging machine performanceOutstanding opacity, white background and reduced show-throughExcellent stiffnessIdeal support for normal ink systemsWater based coatingsFeatures: Acrylic CoatingFlavor & Aroma Barrier Light BarrierApplications:BakeryBiscuits/Cookie/CrackersBox Overwrap Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Health and Beauty Care Household and Detergents Pet Food Uses:Box Overwrap Flexible PackagingHFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	0.497 g/m²/day @Temperature 23.0 °C	0.0320 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	2.95 g/m²/day @Temperature 38.0 °C	0.190 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	650 cc/m²/day @Temperature 23.0 °C	41.9 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	652 cc/m²/day @Temperature 23.0 °C	42.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	50.8 microns	2.00 mil	ExxonMobil Method
Coating Weight	37.9 g/m²	23.7 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	170 %	170 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	55 %	55 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	1.70 GPa	247 ksi	MD; ExxonMobil Method
	2.80 GPa	406 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	610 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	610 g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Brugger, 0.5 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	105 MPa	15200 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	185 MPa	26800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	4.0 % @Temperature 135 °C, Time 432 sec	4.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	2.0 % @Temperature 135 °C, Time 432 sec	2.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Gloss	70 %	70 %	45°; ExxonMobil Method
Transmission, Visible	22 %	22 %	ExxonMobil Method

Descriptive Properties	Value	Comments
Whiteness Index	90
Yield	18300 in²/lb