- Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Semi-Cured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | >= 254 microns | >= 10.0 mil | Side 1 |
| >= 381 microns | >= 15.0 mil | Prime Coated 1523 Fiberglass, Substrate | |
| 635 - 686 microns | 25.0 - 27.0 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 - 70 | 60 - 70 | Compound Property |
| Tensile Strength | 6.21 - 7.58 MPa | 900 - 1100 psi | Compound Property |
| Elongation at Break | 225 - 275 % | 225 - 275 % | Compound Property |
| Peel Strength | >= 1.67 kN/m | >= 9.50 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 7.87 kV/mm | >= 200 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 24.8 - 27.8 | |
| Uncoated Fabric Break Strength | 300 lb/in | Fill Direction, Substrate Property |
| 450 lb/in | Warp Direction, Substrate Property |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound
- Pyrotek ISOMAG® 70 Structural Insulation
- Mearthane Durethaneâ„¢ S DS-680A Solid Polyurethane Elastomer
- A. Schulman PP 2407 Polypropylene Impact Resistant Copolymer Polypropylene
- Polyram PlusTek PA810 Nylon 6.6, Impact Modified
- CIMBAR RiverCal™ 8107 & 8107C Calcium Carbonate (CaCO3)
- BASF Elastollan SP 806 TPUR
- Global NM-3255 High Density Polyethylene, Yarn/Tape Grade (discontinued **)
- A. Schulman POLYTROPE™ TPP 1024E-01 Olefinic Elastomer For Sheet Extrusion
Copyright © lookpolymers.com All Rights Reserved