Adell DR-16 30% Glass Reinforced Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell DR-16 30% Glass Reinforced Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.17 % | 0.17 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0017 cm/cm | 0.0017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 92 | 92 | ASTM D785 |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm @Thickness 3.17 mm |
2.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 760H (NG) Synthetic Oil
- Polymax® Maxelast® C4740 TPE, Transparent
- Solvay Specialty Polymers Amodel® ET-1001 HS Polyphthalamide (PPA) Resin, Dry As Molded (discontinued **)
- Karina E 06/30-FC-LMP Blue Color Concentrate for PVC
- LATI Latamid 66 H2 G/25-V0CT1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Asia Pacific)
- Ultracor® UQF-95-1/4-3.0 Honeycomb Core Material
Copyright © lookpolymers.com All Rights Reserved