- Polykemi AB POLYelast TPE Z650A Thermoplastic Elastomer, SEBS-based, Co-injection Grade
Polykemi AB POLYelast TPE Z650A Thermoplastic Elastomer, SEBS-based, Co-injection Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z650A Thermoplastic Elastomer, SEBS-based, Co-injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | With Flow; ISO 2577 |
| 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 @Time 15.0 sec |
65 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 10.0 MPa | <= 1450 psi | ISO/R527 |
| Elongation at Break | 700 % | 700 % | ISO/R527 |
| 100% Modulus | 0.00250 GPa | 0.363 ksi | ISO/R527 |
| 300% Modulus | 0.00330 GPa | 0.479 ksi | ISO/R527 |
| Tear Strength | 25.0 kN/m | 143 pli | D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | in desiccant air dryer |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SA300S20 Silver-coated Aluminum Granules
- Arkema Group Oroglas® MI-4T Acrylic, Heat Resistant (discontinued **)
- Styron Pulse® 840P ABS + Polycarbonate
- A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene
- A. Schulman PP 828-31 Polypropylene Black Molding Grade Impact Polypropylene
- Esstech X-866-0000 Distilled N, N - Dihydroxyethyl-Para-Toluidine, C11H17NO2
- Dow ISONATE™ 125M Pure MDI
- Fainplast Compounds GA 89 Flexible PVC, Flame Retardant Sheathing
- BASF Heligoen® Blue L 6920 Color Additive
- Beijing Ranger Chem PBT-201-G15 291 Flame Retarding FR PBT
Copyright © lookpolymers.com All Rights Reserved