Arlon 19096R022 0.022" (0.559 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 19096R022 0.022" (0.559 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone RubberThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	76.2 microns	3.00 mil	Side 1
	76.2 microns	3.00 mil	Polyethylene Interleave
	>= 127 microns	>= 5.00 mil	Side 2
	356 microns	14.0 mil	Prime Coated 1523 Fiberglass, Substrate
	521 - 597 microns	20.5 - 23.5 mil	Overall

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40 - 50	40 - 50	Compound Property
Tensile Strength	>= 5.52 MPa	>= 800 psi	Compound Property
Elongation at Break	>= 500 %	>= 500 %	Compound Property
Peel Strength	>= 1.05 kN/m	>= 6.00 pli	Bond Strength

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability Test	<= 3.0	<= 3.0	[in], Char Length; FAR 25.853, Appendix F, Part 1, Section A.1.ii
	<= 15	<= 15	[sec], Flame Time; FAR 25.853, Appendix F, Part 1, Section A.1.ii

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	24.5 - 27.5
Uncoated Fabric Break Strength	300 lb/in	Fill Direction, Substrate Property
	450 lb/in	Warp Direction, Substrate Property