Arkema Group Pebax® Rnew 55R53 SP 01 Polyether Block Amide (PEBA)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer Arkema
Trade Name Pebax®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Pebax® Rnew 55R53 SP 01 Polyether Block Amide (PEBA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether block amide Pebax® 55R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Water Absorption 1.5 %

@Temperature 23.0 °C,
Time 86400 sec
1.5 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.70 %

@Temperature 20.0 °C
0.70 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.010 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.010 in/in

@Thickness 0.157 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.010 in/in

@Thickness 0.157 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 53
53
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
51

@Time 15.0 sec
51

@Time 0.00417 hour
Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 45.0 MPa
6530 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break >= 400 %
>= 400 %
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus 0.160 GPa
23.2 ksi
Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
ISO 11357
Vicat Softening Point 156 °C

@Load 1.02 kg
313 °F

@Load 2.25 lb
ISO 306
Component Elements Properties Metric English Comments
Carbon, C 62 - 66 %
62 - 66 %
Renewable; ASTM 6866
Processing Properties Metric English Comments
Processing Temperature 220 °C
428 °F
Recommended Extrusion Temperature
210 - 230 °C
410 - 446 °F
Extrusion Range
Nozzle Temperature 200 - 270 °C
392 - 518 °F
240 °C
464 °F
Recommended
Mold Temperature 25.0 - 60.0 °C
77.0 - 140 °F
Drying Temperature 65.0 - 75.0 °C
149 - 167 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour