BNZ Materials Blazecrete 3000 G Dense Castable

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Blazecrete
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	BNZ Materials Blazecrete 3000 G Dense Castable.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Blazecrete 3000 G is high alumina castable for service to 3000°F (1667°C). Used in building new and repairing old refractory linings, for gunningInformation provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	2.08 g/cc	0.0752 lb/in³

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00690 GPa	1.00 ksi	At Use Limit; ASTM C268
	0.000700 GPa <br>@Temperature 540 °C	0.102 ksi <br>@Temperature 1000 °F	Fired; ASTM C268
	0.000700 GPa <br>@Temperature 815 °C	0.102 ksi <br>@Temperature 1500 °F	ASTM C268
	0.000900 GPa <br>@Temperature 1095 °C	0.131 ksi <br>@Temperature 2003 °F	ASTM C268
	0.00140 GPa <br>@Temperature 104 °C	0.203 ksi <br>@Temperature 219 °F	Dried; ASTM C268
	0.00140 GPa <br>@Temperature 1260 °C	0.203 ksi <br>@Temperature 2300 °F	ASTM C268
	0.00170 GPa <br>@Temperature 1371 °C	0.247 ksi <br>@Temperature 2500 °F	ASTM C268
Compressive Strength	6.20 MPa <br>@Temperature 815 °C	899 psi <br>@Temperature 1500 °F	Cold Crush Strength
	6.20 MPa <br>@Temperature 1095 °C	899 psi <br>@Temperature 2003 °F	Cold Crush Strength
	8.30 MPa <br>@Temperature 1260 °C	1200 psi <br>@Temperature 2300 °F	Cold Crush Strength
	10.3 MPa <br>@Temperature 1371 °C	1490 psi <br>@Temperature 2500 °F	Cold Crush Strength
	34.5 MPa <br>@Temperature 1667 °C	5000 psi <br>@Temperature 3033 °F	Cold Crush Strength; At Use Limit
	7.60 MPa <br>@Treatment Temp. 540 °C	1100 psi <br>@Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C
	8.30 MPa <br>@Treatment Temp. 104 °C	1200 psi <br>@Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1649 °C	3000 °F
Shrinkage	1.0 %	1.0 %	Permanent Linear Change at Use Limit; ASTM C210
	0.10 % <br>@Temperature 104 °C	0.10 % <br>@Temperature 219 °F	Permanent Linear Change; ASTM C210
	0.10 % <br>@Temperature 540 °C	0.10 % <br>@Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.10 % <br>@Temperature 815 °C	0.10 % <br>@Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.30 % <br>@Temperature 1095 °C	0.30 % <br>@Temperature 2003 °F	Permanent Linear Change; ASTM C210
	0.50 % <br>@Temperature 1260 °C	0.50 % <br>@Temperature 2300 °F	Permanent Linear Change; ASTM C210
	0.90 % <br>@Temperature 1371 °C	0.90 % <br>@Temperature 2500 °F	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English
Al2O3	53.9 %	53.9 %
CaO	2.0 %	2.0 %
Fe2O3	1.7 %	1.7 %
SiO2	38 %	38 %
TiO2	2.6 %	2.6 %