SCG Chemicals EL-Leneâ„¢ H5211P High Density Polyethylene Pipe Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H5211P High Density Polyethylene Pipe Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: Good processing, high thermal stabilityRecommended Applications: Water pipes, conduit, sewage drainage pipesInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 10000 hour | >= 10000 hour | F0; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 40 min @Temperature 200 °C |
>= 40 min @Temperature 392 °F |
ISO/TR10837 |
| Melt Flow | 0.44 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.44 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Crosshead speed 100 mm/min; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | Crosshead speed 100 mm/min; ISO 527 |
| Elongation at Break | 815 % | 815 % | Crosshead speed 100 mm/min; ISO 527 |
| Flexural Modulus | 0.960 GPa | 139 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Temperature -20.0 °C |
1.84 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 1.86 J/cm @Temperature 0.000 °C |
3.49 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 2.26 J/cm @Temperature 23.0 °C |
4.22 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Hydrostatic Design Basis | 8.00 MPa | 1160 psi | MRS Classified; ISO 9080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |
Users viewing this material also viewed the following:
- Overview of materials for Phenolic; Unreinforced; Molded
- DSM Akulon® K-FG6 (Dry) 30% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Materion Beryllium Copper Alloy 174 Strip; 1/2HT (TH02) Temper (UNS C17410)
- Gwent Electronic Materials P2121112P6 Oxygen Plasma Modified Graphene Nanoplatelets
- Techmer ES HiFill® PPA GF30 HS L 30% Glass Filled
- TIMCAL TIMREX® T200-2000 Primary Synthetic Graphite
- A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
- Fainplast Compounds GS 38/T Flexible PVC, Injection Molding for Transparent Technical Items
- E-Polymers TEKAFIN® PH40FR Flame Retardant Heat Resistance Compounded-PP
Copyright © lookpolymers.com All Rights Reserved