Addiplast Addinyl B2 V30 Nylon 6, 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl B2 V30 Nylon 6, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, high strengthInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | Conditioned; ISO 868 |
| 83 | 83 | ISO 868 | |
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO R 527 |
| 170 MPa | 24700 psi | ISO R 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO R 527 |
| 5.0 % | 5.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 4.80 GPa | 696 ksi | Conditioned; ISO 178 |
| 8.20 GPa | 1190 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A |
| 22.0 kJ/m² | 10.5 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/IeU |
| 7.50 J/cm² | 35.7 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/IeA |
| 1.90 J/cm² | 9.04 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM E831 |
| Melting Point | 220 °C | 428 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-2/AF |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; CEI 60243-1 |
| 35.0 kV/mm | 889 kV/in | CEI 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Pau Tai Unistab ECZ-660 Calcium-Zinc/Barium-Zinc
- A. Schulman POLYBATCH™ Blue LL40299U/3 Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- A. Schulman POLYFORT™ FPP 3708U UV Stable Copolymer Polypropylene
- Unipetrol C4 Fraction
- 3M AC-215 Class B-1/2 Aerospace Sealant
- Alliance Polymers Viprene™ G40D-32U-NAT Thermoplastic Vulcanizate Elastomer
- Ametek P316L P/M Stainless Steel, Sintered from 6.83 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved