Samsung Cheil Industries Infino® HP-1000H PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HP-1000H PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 14 g/10 min @Load 10.0 kg, Temperature 250 °C |
14 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength at Break | 61.8 MPa | 8960 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.9 MPa | 7820 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 113 % | 113 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.20 J/cm @Thickness 6.35 mm |
9.74 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 6.08 J/cm @Thickness 3.17 mm |
11.4 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 134 °C | 273 °F | B/50; ISO R306 |
| 137 °C | 279 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 26 A Linear Low Density Polyethylene
- ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder (discontinued **)
- SCG Chemicals EL-Leneâ„¢ S10 Butene (C4) Rotational Molding Resin
- Dow Corning HV 1760/80 SILICONE RUBBER NATURAL
- ChevronTexaco Canopus® 150
- ExxonMobil LL 8555.25 Rotational Molding Resin
- Epoxy Technology EPO-TEK® H20-LC Electrically Conductive, Silver Epoxy
- Dow DOWLEX™ 2056 Linear Low Density Polyethylene, Heavy Duty Film Grade
- LG Chemical HF350U ABS, High Flow
Copyright © lookpolymers.com All Rights Reserved