Addiplast Addilene PMD 50218 Flame Retardant Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene PMD 50218 Flame Retardant Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, unreinforced, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 1183/A |
| Melt Flow | 12 g/10 min | 12 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | Conditioned; ISO 868 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | Conditioned; ISO R 527 |
| Elongation at Break | >= 100 % | >= 100 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 1.20 GPa | 174 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2/AF |
| Vicat Softening Point | 148 °C | 298 °F | ISO 306/A50 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB VC-105 Foam Stabilizer
- NOVA Chemicals Styrocell® B933A Expandable Polystyrene (discontinued **)
- M. Holland Company CP503 Polypropylene Impact Copolymer
- LG Chemical HI100H ABS, High Impact, High Toughness
- Lucite International Lucite® 30B Acrylic Bead Resin
- Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant
- Styrolution Absolac® 30GF30 ABS, 30% Glass Filled
- A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
- H.C. Starck Amperit® 518.054 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
Copyright © lookpolymers.com All Rights Reserved