SABIC Innovative Plastics LNP Stat-kon DS0029 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DS0029 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DS0029 is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | 23°C / 50% RH; ISO 62 |
| 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm @Time 86400 sec |
0.0065 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0073 cm/cm @Time 86400 sec |
0.0073 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 7.8 % | 7.8 % | 5 mm/min; ISO 527 |
| 13.2 % | 13.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.1 % | 5.1 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.32 GPa | 336 ksi | 1 mm/min; ISO 527 |
| 2.55 GPa | 370 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.23 GPa | 323 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.930 J/cm @Temperature 23.0 °C |
1.74 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 16.0 J/cm @Temperature 23.0 °C |
30.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 88.0 kJ/m² @Temperature 23.0 °C |
41.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 - 6.0 ohm | 3.0 - 6.0 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Chevron Phillips HiD® 99413F with Food Grade Antistat HDPE Blow Molding Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7336/GY7016 PEEK, with glass fiber
- Lucite International Colacryl ® TS1631 Acrylic Solution Resin
- LATI Latilub 87/28-15T K/20 PC, 20% Carbon Fiber Reinforced, PTFE Filled
- Teknor Apex APEX® 89-P180-B Polyvinyl Chloride, Flexible
- Samyang Triel® 5600 Thermoplastics Polyetherester Elastomer, General Extrusion
- Tra-Con Tra-Bond 293-21 General Purpose Epoxy Adhesive
- ChevronTexaco Rando® HD 46 Ashless
- 3M XP2112 Hi-Performance Adhesive Transfer Tape
- Zoltek Pyron® Plain Weave Fabric Oxidized Pan Fiber
Copyright © lookpolymers.com All Rights Reserved