Addiplast Addilene H 210 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 210 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UnreinforcedInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183/A |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO R 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO R 527 |
| Elongation at Yield | >= 100 % | >= 100 % | ISO R 527 |
| Modulus of Elasticity | 1.25 GPa | 181 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/IeU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | CEI 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Menzolit Menzolit® BMC 1650 Unsaturated Polyester UP
- Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F)
- Shakespeare MX-200 PP Polypropylene Monofilament
- Saint-Gobain CHR® 2265-5 Extruded PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- UBE UMERIT 613A Metallocene LLDPE
- Covestro Makrolon® FR6901 Polycarbonate
- BASF Heligoen® Blue K 6911 D Color Additive
- Ceramic Process Systems AlSiC-8, 70 vol% SiC
Copyright © lookpolymers.com All Rights Reserved